KC-301 Due to its high water resistance, desirable flexibility, good permeability and high adhesion strength which Has a variety of cellulose pads for use in cooling systems, gas turbine coolers, pads which use for greenhouses, poultry pads and ect.
Technical Specifications
| value | unit | test method | |
| Solid Percentage | 39-41 | % | ISO 1625 |
| PH | 6-7 | Nu | ISO 976 |
| Viscosity | 6000-8000 | Centipede | ISO 2555 |
| Density | 1.01 | Gr/cm3 | ISO 2811 |
| MFFT | 5 | ˚𝑐 | ASTM D2354 |
Product Specifications
The type of depression: Anionic
Plasticizer: No plasticizer
Pad permeability: very good
Flexibility: Required
Compatibility: kc-301 Mixed with many water based anionic and nonionic polymers.
Concentrators: kc-301with a variety of acrylic acid, polyvinyl alcohol, cellulose ethers and concentrator Polyurethane viscosity are compatible.
Plasticizers: kc-301 is compatible with all types of glycol ether, phthalates and benzoates.
Coagulation Agents: kc-301 is compatible with a variety of coagulation agents including texanol, polymers
402, diethylene glycol mono butyl ether.
Description
during using KC-301 depending on the usage, it can be possible to reduce the film formation temperature by coagulation factors and reach the appropriate concentration using thickeners. Proper preservatives
should be used when used and to prevent micro-organisms from attacking. Glycols should be used. It increases frost resistance but generally does not reduce the film formation temperature.
Storage
The standard KC- 301 resin has a shelf life of six months from production date under standard warehouse conditions. The resin should be protected from freezing and direct sunlight. The container should be completely closed after each use.